Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the premium-addons-for-elementor domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home/pacificmetalind/public_html/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the rocket domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home/pacificmetalind/public_html/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home/pacificmetalind/public_html/wp-includes/functions.php on line 6114
Stainless Steel Composition Percentage - Pacific Metal

:root{--wpr-bg-7ff30b6b-8cf0-4677-90c7-d2f22e09dc5a: url('https://www.pacificmetalindia.com/wp-content/uploads/2021/02/technical-info-banner.jpg');}:root{--wpr-bg-8284a54b-6307-459f-97f7-6d8a1ac87cf8: url('https://www.pacificmetalindia.com/wp-content/uploads/2021/01/cropped-industry.jpg');}

TECHNICAL INFO

TECHNICAL INFO

Chemical Composition ( IN PERCENTAGE )

Stainless Steel

Grade	C (Max)	Mn (Max)	P (Max)	S (Max)	Si (Max)	Cr	Ni	Mo	Nitrogen (Max)	Cu/ Others
301	0.15	2.00	0.045	0.030	1.00	16.00 – 18.00	6.00 – 8.00	-	0.10	-
304	0.08	2.00	0.045	0.030	0.75	18.00 – 20.00	8.00- 10.50	-	0.10	-
304L	0.030	2.00	0.045	0.030	0.75	18.00 – 20.00	8.00- 12.00	-	0.10	-
310S	0.08	2.00	0.045	0.030	1.50	24.00- 26.00	19.00 – 22.00	-	-	-
316	0.08	2.00	0.045	0.030	0.75	16.00 – 18.00	10.00 – 14.00	2.00 – 3.00	0.10	-
316L	0.030	2.00	0.045	0.030	0.75	16.00 – 18.00	10.00 – 14.00	2.00 – 3.00	0.10	-
317	0.08	2.00	0.045	0.030	0.75	18.00 – 20.00	11.00 – 14.00	3.00 – 4.00	0.10	-
317L	0.030	2.00	0.045	0.030	0.75	18.00 – 20.00	11.00 – 15.00	3.00 – 4.00	0.10	-
321	0.08	2.00	0.045	0.030	0.75	17.00 – 19.00	9.00 – 12.00	-	0.10	Ti5 ( C + N ) Min or 0.70 max
347	0.08	2.00	0.045	0.030	0.75	17.00 – 19.00	9.00 – 13.00	-	-	Cb= 10x ( C Min ) or 1.00 Max
409	0.08	1.00	0.040	0.010	1.00	10.50 – 11.75	0.50	-	-	Ti= 6x (C+ N ) Min or 0.70 Max
409M	0.03	0.81.2	0.030	0.030	0.40.75	11.00- 12.00	1.5 max.	-	-	Ti= 6x (C) Min or 0.70 Max
410S	0.08	1.00	0.040	0.030	1.00	11.50- 13.50	0.60	-	-	-
410	0.15	1.00	0.040	0.030	1.00	11.50- 13.50	0.75	-	-	-
420	0.35	0.50	0.035	0.015	0.50	12.00 – 13.00	0.20.3	-	-	-
430	0.12	1.00	0.040	0.030	1.00	16.00 – 18.00	0.75	-	-	-
JSL AUS	0.08	7.08.0	0.070	0.030	0.75	15.50 – 16.50	4.25 – 4.75	-	-	0.9 – 1.10
JS- 203	0.08	9.2510.25	0.070	0.030	0.75	14.25 – 15.25	2.25 – 2.75	-	-	1.60- 2.0
301M	0.10	4.55.5	0.060	0.030	0.75	14.50 – 15.50	6.0 – 7.0	-	-	1.70- 1.90
* Thickness of 1.27mm & below will have elongation of 20% min.